Sikaplan® WP 1100-25 HL2
Sikaplan® WP 1100-25 HL2 is a flexible, 2.5 mm thick, homogeneous sheet waterproofing membrane. It contains a ≤ 0.2 mm thick signal layer and is based on high-quality polyvinylchloride (PVC-p).
- Certified for öBV tunnel guidelines, table 4.6 and table 4.7
- Contains no recycled materials and no DEHP (DOP) plasticisers
- Proven performance over decades
- High resistance to ageing
- Good resistance to microbial degradation
- Good resistance to root penetration
- Flexible in cold temperatures
- Suitable for contact with acidic (soft) water and alkaline environments
- Optimised flexibility, tensile strength and multi-axial elongation
- Optimised workability and thermally weldable
Usage
The Product is designed for:- Waterproofing of basements against water ingress
- Waterproofing of tunnels against water ingress
Advantages
- Certified for öBV tunnel guidelines, table 4.6 and table 4.7
- Contains no recycled materials and no DEHP (DOP) plasticisers
- Proven performance over decades
- High resistance to ageing
- Good resistance to microbial degradation
- Good resistance to root penetration
- Flexible in cold temperatures
- Suitable for contact with acidic (soft) water and alkaline environments
- Optimised flexibility, tensile strength and multi-axial elongation
- Optimised workability and thermally weldable
Packaging
Roll width | 2 m |
Roll length | specified |
Colour
Surface texture | smooth |
Signal layer colour | yellow |
Bottom layer colour | black |
Product Details
APPROVALS / CERTIFICATES
CE Marking and Declaration of Performance to EN 13491 - Geosynthetic barriers — Characteristics required for use as a fluid barrier in the construction of tunnels and underground structures
CE Marking and Declaration of Performance to EN 13967 — Flexible sheets for waterproofing - Damp proofing and basement tanking
Meets the requirements according to the öBV Directive "Tunnelabdichtung", table 4-6, issued in December 2012
Meets the requirements according to the öBV Directive "Tunnelabdichtung", table 4-7, issued in December 2012
Fulfils the requirements of annex C.5 of SIA 272:2009
Composition / Manufacturing
PVC-p
Shelf Life
5 years from date of production
Storage Conditions
The Product must be stored in original unopened and undamaged sealed packaging in dry conditions and temperatures between +5 °C and +35 °C. Protect the Product from direct weather exposure. Store in a horizontal position. Do not stack pallets of the rolls on top of each other, or under pallets of any other materials during transport or storage. Always refer to packaging.
Effective Thickness
2.50 mm (-0.12 mm / +0.25 mm) including signal layer | (EN 1849-2) |
Signal layer thickness | ≤ 0.2 mm |
Mass per unit area
3.25 kg/m² (-0.16 kg/m² / +0.32 kg/m²) | (EN 1849-2) |
System Structure
The Product is part of Sikaplan® WP compartmentalised waterproofing system.
Resistance to Impact
Method A, 500 g falling weight | Watertight at 750 mm drop height |
Resistance to Static Puncture
> 2.5 kN | (EN ISO 12236) |
Long Term Compression Strength
Water tightness, aged 48 hours | Watertight at 7.0 N/mm² |
Tensile Strength
Longitudinal (MD) | 17 N/mm² ± 2 N/mm² |
Transversal (CMD) | 16 N/mm² ± 2 N/mm² |
Longitudinal (MD) | 17 N/mm² ± 2 N/mm² |
Transversal (CMD) | 16 N/mm² ± 2 N/mm² |
Burst Strength
D = 1.0 m | ≥ 80 % |
Service Temperature
Minimum | -10 °C |
Maximum | +35 °C |
Ambient Maximum Temperature of Liquids
+35 °C
Foldability
No cracks at -20 °C | (EN 495-5) |
Watertightness
Method B: 24 hours at 60 kPa | Pass |
Water Permeability
< 10-6 m3·m-2·d-1 | (EN 14150) |
Chemical Resistance
Change in tensile strength and elongation, 0.5 % sulphuric acid test, aged 360 days at +50 °C | < 20 % |
Change in mass, 0.5 % sulphuric acid, aged 360 days at +50 °C | < 4 % |
Change in tensile strength, 5-6 % sulphurous acid test, aged 90 days at +23 °C | < 20 % |
Foldability at low temperatures, 5-6 % sulphurous acid test, aged 90 days at +23 °C | No cracks at -20 °C |
Change in impact load, 0.5 % sulphuric acid, aged 360 days at +50 °C | ≤ 30 % |
Change in impact load, saturated lime wash, aged 360 days at +50 °C | ≤ 30 % |
Change in tensile strength and elongation, saturated lime wash, aged 360 days at +50 °C | < 20 % |
Change in mass, saturated lime wash, aged 360 days at +50 °C | < 4 % |
Behaviour after Storage in Warm Water
Change in tensile strength, aged 360 days at +70 °C | < 20 % |
Change in elongation, aged 360 days at +70 °C | < 20 % |
Change in mass, aged 360 days at +70 °C | < 4 % |
Reduction of impact load, aged 360 days at +70 °C | ≤ 30 % |
Dimensional change, aged 360 days at +70 °C | < 2 % |
Resistance to Oxidation
Change in tensile strength, aged 90 days at +85 °C | < 10 % |
Change in elongation, aged 90 days at +85 °C | < 10 % |
Foldability at low temperatures, aged 90 days at +85 °C | No cracks at -20 °C |
Microbiological Resistance
Change in tensile strength, aged 16 weeks | < 15 % |
Change in elongation, aged 16 weeks | < 15 % |
Durability of Watertightness against Chemicals
Calcium hydroxide, aged 28 days at +23 °C, tested 24 hours at 60 kPA | Pass |
Resistance to UV Exposure
Not permanently UV stable
Resistance to Weathering
Not resistant to permanent weathering
Behaviour after heat welding
Behaviour of weld in shear test | Break occurs outside the seam |
Peel resistance of welded seam | > 6.0 N/mm |
Dimensional Change after Heat
Longitudinal (MD), aged 6 hours at +80 °C | < 2 % |
Transversal (CMD), aged 6 hours at +80 °C | < 2 % |
Blisters, aged 6 hours at +80 °C | No blisters |
Durability of Watertightness against Ageing
Aged 12 weeks at +70 °C, tested 24 hours at 60 kPa | Pass |
Reaction to Fire
Class E | (EN 13501-1) |
Application
APPLICATION INSTRUCTIONS
IMPORTANT
Strictly follow installation procedures
Strictly follow installation procedures as defined in Method Statements, application manuals and working instructions which must always be adjusted to the actual site conditions.
SUBSTRATE QUALITY
For information on substrate quality / pre-treatment, refer to the following Sika® method statement:
-
Sikaplan® WP sheet membrane (PVC) system for waterproofing basements and other below ground structures
-
Sikaplan® WP sheet membrane (PVC) system for waterproofing tunnels
APPLICATION
For information on application, refer to the following Sika® method statement:
Sikaplan® WP sheet membrane (PVC) system for waterproofing basements and other below ground structures
Sikaplan® WP sheet membrane (PVC) system for waterproofing tunnels
IMPORTANT
Application by trained personnel
The application of this Product must only be carried out by Sika® trained and/or approved contractors, experienced in this type of application.
IMPORTANT
Ventilation in confined spaces
Always ensure good ventilation when applying the Product in a confined space.
IMPORTANT
Not resitant to bitumen and plastics
The Product is not resistant to permanent contact with bitumen and some types of plastics other than PVC.
- For use over or adjacent to these materials, apply a separation layer of polypropylene geotextile (≥ 150 g/m²).