Sikaflex® Max Hybrid 1

MULTI-PURPOSE ADHESIVE/SEALANT BASED ON HYBRID POLYMER TECHNOLOGY

Sikaflex® Max Hybrid 1 is a one-component, high-performance, multi-purpose, all-weather hybrid polymer adhesive/sealant. Its advanced technology offers maximum flexibility and superior adhesion for most construction material substrates.

  • Resists to extreme temperatures from -40 °C (-40 °F) to 90 °C (194 °F)
  • Very good UV resistance
  • Excellent resistance to aging and weathering
  • Excellent adhesion – bonds to most construction materials without a primer
  • Flexible and easy-to-apply
  • Bubble-free, even in wet and humid conditions
  • No shrinkage, non-sag, no surface tackiness
  • Does not contain isocyanate
  • Low VOC-content
  • Non-staining
  • Paintable with water-based paints
Buy In Store
Product Data Sheet Show all documents

Usage

Bonds and seals most construction material substrates including concrete, masonry, aluminum, metals, ceramics, porcelain, granite, marble, PVC, glass, and wood. Suitable for a wide range of applications, such as windows and doors frames, concrete joints, metal building construction, roofing and gutter, HVAC, general sealing and waterproofing.  

Advantages

  • Resists to extreme temperatures from -40 °C (-40 °F) to 90 °C (194 °F)
  • Very good UV resistance
  • Excellent resistance to aging and weathering
  • Excellent adhesion – bonds to most construction materials without a primer
  • Flexible and easy-to-apply
  • Bubble-free, even in wet and humid conditions
  • No shrinkage, non-sag, no surface tackiness
  • Does not contain isocyanate
  • Low VOC-content
  • Non-staining
  • Paintable with water-based paints

Packaging

290 mL (9.8 US fl. oz) cartridge, 12 cartridges per box

Colour

Black, Dark Bronze

Product Details

Sustainability / Certifications / Approvals

ENVIRONMENTAL INFORMATION

Conformity with LEED v4.1 EQc Low-Emitting Materials
Product Information

Composition / Manufacturing

Polyurethane and Silicone based

Shelf Life

12 months in original unopened packaging

Storage Conditions

Store in original, unopened and undamaged packaging in dry conditions at temperatures between 5 °C (41 °F) and 25 °C (77 °F). 

Density

1.60 g/l (0.013 lb/gal)
Technical Information

Shore A Hardness

40 ± 5

(ISO 868)

Tensile Strength

1.5 - 2.0 MPa (218 - 290 psi)

(DIN 53504)

Shrinkage

< 3 %

(ISO 10563)

Temperature Resistance

-40 °C (-40 °F) to 90 °C (194 °F)

Joint Design

The minimum joint width and depth are 5 mm (3/16 in). The typical joint dimension follow a width-to-depth ratio of 2:1

Elongation at break

≥ 300 %

(DIN 53504)

Curing Conditions

Cure at room temperature with moisture

Application

Application Information

Backing Material

To be used with Sikaseal®-414 Backer Rod

Sagging

0 mm (0 in)

(ISO 7390)

Ambient Air Temperature

5 °C (41 °F) to 40 °C (104 °F)

Curing Rate

Min. 2.5 mm/24h (23 °C (73 °F) and 50 % R.H.)

Skinning time

12 - 25 min (23 °C (73 °F) and 50 % R.H.)
Consumption

Yield

Bonding:

Yield per cartridge

Dimension

~118 spots

Diameter = 25 mm (1 in)

Thickness = 5 mm (3/16 in)

~14.8 m (48.6 ft) bead

Diameter = 5 mm (3/16 in) (Cylindrical)

  

Sealing, l.m. (l.ft) per cartridge:

Depth mm (in)

Width mm (in)

6 (1/4)

13 (1/2)

19 (3/4)

25 (1)

32 (1 1/4)

6 (1/4)

8.1 (26.5)

-

-

-

-

13 (1/2)

3.7 (12.1)

1.7 (5.6)

-

-

-

19 (3/4)

2.5 (8.2)

1.2 (3.9)

0.8 (2.6)

-

-

25 (1)1.9 (6.2)0.9 (3.0)0.6 (2.0)0.5 (1.6)-
32 (1 1/4)1.5 (4.9)0.7 (2.3)0.5 (1.6)0.4 (1.3)0.3 (1.0)

Consumption depends on the roughness and absorbency of the substrate. These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level or wastage etc.
Application steps

SUBSTRATE PREPARATION

GlassDegrease with alcohol or MEK
Aluminium, light alloys and stainless steel

Degrease with alcohol or MEK

Other MetalsLightly abrade then degrease as above
WoodLightly abrade surface then remove dust
PlasticsDegrease using an agent recommended by plastics manufacturer
Concrete and other alkaline SurfacesThe substrate must be sound, clean, dry and free of all contaminants such as dirt, oil, grease, cement laitance, old sealants and poorly bonded paint coatings which could affect adhesion. The substrate must be of sufficient strength to resist with the stresses induced by the adhesive/sealant during movement. Use removal techniques such as wire brushing, grinding, sanding, or other suitable mechanical methods. All dust, loose and friable material must be completely removed from all surfaces before application.

CLEAN UP

Clean all tools and equipment with a paint thinner / solvent. Once hardened, the product can only be removed mechanically. Wash soiled hands and skin thoroughly in hot soapy water or use Sika® Cleaning Wipes-120.