Sarnafil® S 327-60 Textured
60 mil thick PVC thermoplastic membrane with textured top surface
Sarnafil® S 327-60 Textured Roof Membrane is a PVC thermoplastic membrane produced with an integral polyester reinforcement for high strength, with heat‐weldable seams, and a textured surface.
- Embossed surface
- Excellent tear strength resistance
- Hot‐air welded seams for long‐term performance
- Superior fire resistance
- Proven membrane performance
Usage
Mechanically attached applications with various fastening methods, over various substrates. It can also be used in adhered applications to approved substrates. AREAS OF APPLICATION- In-seam disc systems
- In-seam batten, double-weld systems
- RhinoBond® systems
- New construction and reroofing
Advantages
- Embossed surface
- Excellent tear strength resistance
- Hot‐air welded seams for long‐term performance
- Superior fire resistance
- Proven membrane performance
Packaging
60 mil (1.5 mm) Membrane*(Reflective Gray)
10 ft x 100 ft (3.05 m x 30.5 m) roll, 390.22 lbs (177 kg) per roll,
8 rolls per pallet
5 ft x 100 ft (1.52 m x 30.5 m) roll, 195.11 lbs (88.5 kg) per roll,
12 rolls per pallet
60 mil (1.5 mm) Membrane*(White and Reflective Gray)
6.56 ft x 65.6 ft (2 m x 20 m) roll, 168 lbs (76 kg) per roll,
19 rolls per pallet
* Made to order, minimum volume required, extended production lead times. Consult with Sika – Roofing representative for further information.
Colour
- Top: White, Gray, and Tan
- Bottom: Dark Gray
Product Details
APPROVALS / CERTIFICATES
- FM Global
- Underwriters Laboratories
- Underwriters Laboratories Canada
- ICC Code Compliance – ESR 1157
- Miami‐Dade County
- Florida Building Code
- LEED / Green Globes
- NSF/ANSI 347 : Platinum Certified
- CGSB-37.54-95. Type 4/Class B
- CSA-A123.21
Composition / Manufacturing
High quality, PVC membrane containing ultraviolet light stabilizers, flame retardant and polyester scrim reinforcement
Reinforcing Material
Polyester
Shelf Life
N/A
Storage Conditions
Store rolls on pallets and fully protected from the weather with clean canvas tarpaulins. Unvented polyethylene tarpaulins are not accepted due to the accumulation of moisture beneath the tarpaulin in certain weather conditions that may affect the ease of membrane weldability.
Top surface
Textured
Overall Thickness
| 60 mil (1.5 mm), minimum thickness 45 mil | (ASTM D-751) (ASTM Type III D-4434 Spec. Requirement) |
Thickness Above Scrim
| Exceed 16 mil | (ASTM D-7635) (ASTM Type III D-4434 Spec. Requirement) |
Resistance to Static Puncture
| Pass 33 lbf (15 kg) | (ASTM D-5602) (ASTM Type III D-4434 Spec. Requirement) |
Resistance to Dynamic Puncture
| Pass 14.7 ft-lbf (20 J) | (ASTM D-5635) (ASTM Type III D-4434 Spec. Requirement) |
Tensile Strength
| 305 lbf (1356 N) 200 lbf (890 N) | (ASTM D-751) (ASTM Type III D-4434 Spec. Requirement) |
Tear Strength
| 48 lbf (213 N) 45 lbf (200 N) | (ASTM D-751) (ASTM Type III D-4434 Spec. Requirement) |
Seam Strength
| Pass 75% of original1 | (ASTM D-751) (ASTM Type III D-4434 Spec. Requirement) |
1 Failure occurs through membrane rupture not seam failure.
Linear Dimensional Change
| -0.12% 0.5% | (ASTM D-1204) (ASTM Type III D-4434 Spec. Requirement) |
Low Temperature Flexibility
| Pass Pass ‐40°F (‐40°C) | (ASTM D-2136) (ASTM Type III D-4434 Spec. Requirement) |
Weight Change after Immersion in Water
| Pass ± 3.0% | (ASTM D-570) (ASTM Type III D-4434 Spec. Requirement) |
Resistance to UV Exposure
| 10,000 hours 5,000 hours | (ASTM G-154) (ASTM Type III D-4434 Spec. Requirement) |
| Cracking (7x magnification) | None |
| Crazing (7x magnification) | None |
Retention of Properties after Heat Ageing
| Tensile Strength, % of original: Pass Elongation, % of original: Pass Tensile Strength, % of original: 90 Elongation, % of original: 90 | (ASTM D-751) (ASTM D-751) (ASTM Type III D-4434 Spec. Requirement) |
Application
APPLICATION
Sarnafil S 327 is rolled out onto the insulation board or acceptable substrate, flipped over in order to reveal textured side of membrane as the top surface, fastened to the roof deck with appropriate plates and fasteners, and heat‐welded together by trained operators using hot‐air welding equipment. Please consult Sika’s Specification or Applicator Handbook for detailed installation procedures.