Sika® Icosit® KC 330 Primer CA
Sika® Icosit® KC 330 Primer CA is a 1-pack, polyurethane ready to use, solvented, reaction-curing primer.
- Highly abrasion resistant
- Good penetration and substrate stabilisation
- Moisture-curing
- Tough-hard
Usage
Adhesion promoter as pre-treatment of dry concrete, steel and asphalt substrates. For improving adhesion of the Icosit® KC 330 / 340 range of products.Advantages
- Highly abrasion resistant
- Good penetration and substrate stabilisation
- Moisture-curing
- Tough-hard
Packaging
3 L pail (0.8 US gal.)
Colour
Yellowish-brown / transparent
Product Details
Composition / Manufacturing
1-pack polyurethane
Shelf Life
12 months from date of production
Storage Conditions
The product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +10 °C and +25 °C (50 °F and 77 °F). Always refer to packaging.
Density
~1,0 kg/L | (ISO 2811-1) |
Service Temperature
- -40 °C min. / +80 °C max.
(-40 °F min. / 176 °F max.) - short term up to +150 °C (300 °F)
Temperature Resistance
Dry heat short-term up to approx. +150 °C (300 °F), liquids up to approx. +60 °C (140 °F)
Chemical Resistance
Long-term resistant against:
- Water
- Many detergent solutions
- Seawater
Temporary resistant against:
- Mineral oil
- Diesel fuel
Short-term or no resistance against:
- Organic solvents (esters, ketones, aromates) and Alcohol
- Concentrated lyes and acids
Contact Sika Canada Inc. for specific information.
Application
Product Temperature
Condition product before application preferably at +15 °C (59 °F)
Ambient Air Temperature
+5 °C min. / +35 °C max.
(41 °F min. / 95 °F max.)
Relative Air Humidity
30 % min. / 70 % max.
Substrate Temperature
+5 °C min. / +35 °C max.
(41 °F min. / 95 °F max.)
Substrate Moisture Content
≤ 3 % parts by weight +3 °C max. above dew point temperature
Pot Life
Contents of opened container should be used within the same day.
Waiting Time / Overcoating
At 40 % - 60 % relative humidity
+10 °C (50 °F) | +20 °C (68 °F) | +30 °C (86 °F) | |
Minimum | 3 hours | 1 hour | 1 hour |
Maximum | 3 days | 3 days | 3 days |
Consumption
approx. 0.1 kg/m2 - 0.2 kg/m2 (0.02 lb/ft2 - 0.04 lb/ft2)
Depends on the roughness and absorbency of the substrate.
SUBSTRATE QUALITY
- Substrate must be sound, free from oil, grease, loose and friable particles or any contaminants or conditions that may affect adhesion or overall product performances.
- Concrete tensile strength ≥ 1.5 MPa.
SUBSTRATE PREPARATION
- Concrete substrates must be prepared mechanically to remove cement laitance and achieve an open textured surface (CSP 3 as per ICRI 310-2R).
- Weak cementitious substrates must be removed and surface defects such as blow holes and voids must be fully exposed and filled / repaired with compatible Sika® products.
- Steel substrates must be prepared mechanically using suitable abrasive blast cleaning to remove all corrosion products and achieve a bright metal finish.
- All dust, loose and friable material must be completely removed from all surfaces before application of the product and associated system products, preferably by vacuum extraction equipment.
CLEAN UP
Uncured material can be removed from equipment and tools using Sika® Urethane Thinner and Cleaner. Cured material can only be removed manually or mechanically. For removal of uncured material from hands and sensitive surfaces, use Sika® Hand Cleaner towels.