Sikafloor®-261 CA Thixo Lite

THIXO COATING (ORANGE PEEL TEXTURE) (14 - 17 MIL)

Sikafloor®-261 CA Thixo Lite is a two-component, solid colour, high solids, silicone-free, moderate thixotropic viscosity, glossy epoxy resin available in an unlimited colour range. Typically installed as a seamless, high build, fine orange peel-textured coating for light to medium-duty traffic areas. This general service epoxy coating demonstrates good mechanical and chemical resistance. Final surface appearance options include: unlimited colour selection, integral cove base, gloss, satin or matte surface sheen. Sikafloor®-261 CA Thixo Lite is also used as a top coat for high performance Sikafloor® Morritex Systems.

  • Moderate mechanical and chemical resistance
  • Aesthetic textured finish
  • Hides surface imperfections
  • Durable, impermeable and seamless
  • Easily cleaned, maintained and a more sanitary work environment
  • Neutral odour
  • Unlimited colours, no minimum required
  • Does not support growth of bacteria or fungus
  • Achieves high performance ratings according to ASTM G21 resistance to fungi (Rated 1 [traces of growth]) and ASTM D3273 resistance to mold growth (Rated 10 [highest resistance]) (special order grade)
Product Data Sheet
Show all documents

Usage

  • Wet and dry process areas
  • Commercial and institutional buildings
  • Health care facilities
  • Laboratories
  • Moderate mechanical and chemical resistance areas
  • Recreational centers
  • Showroom areas
 

Advantages

  • Moderate mechanical and chemical resistance
  • Aesthetic textured finish
  • Hides surface imperfections
  • Durable, impermeable and seamless
  • Easily cleaned, maintained and a more sanitary work environment
  • Neutral odour
  • Unlimited colours, no minimum required
  • Does not support growth of bacteria or fungus
  • Achieves high performance ratings according to ASTM G21 resistance to fungi (Rated 1 [traces of growth]) and ASTM D3273 resistance to mold growth (Rated 10 [highest resistance]) (special order grade)

Packaging

30 L (7.9 US gal.) unit
(Sikafloor®-261 CA Thixo Lite Coating consists of a special component B)

Colour

RAL 7038 Agate Grey

RAL 7030 Stone Grey

RAL 7046 Telegrey 2
RAL 7012 Basalt Grey

Custom colours available upon request. Refer to current price list for availability.

Product Details

Sustainability / Certifications / Approvals

ENVIRONMENTAL INFORMATION

  • Conformity with LEED® v4 EQc 2: Low-Emitting Materials
  • Conformity with LEED®v4 MR Credit (Option 2): Building Product Disclosure and Optimization - Sourcing of Raw Materials

APPROVALS / CERTIFICATES

  • Meets the requirements of CFIA and USDA for use in food plants.
Product Information

Shelf Life

2 years in original unopened packaging.

Storage Conditions

Store dry between 5 °C to 32 °C (41 °F to 89 °F). Condition product at temperatures between 18 °C to 30 °C (65 °F to 86 °F) before using.

Volatile organic compound (VOC) content

< 50 g/L
Technical Information

Shore D Hardness

~76

(ASTM D2240)

Abrasion Resistance

~0.11 g (~0.0038 oz)  CS17/1000 cycles/1000 g (2.2 lb)

(ASTM D4060)

Resistance to Impact

~5.42 joules (~3.99 ft lb)

(ASTM D2794)

Indentation

~8 %

(MIL-PRF-24613)

Compressive Strength

~56 MPa (~8122 psi)

(ASTM D695)

Tensile Strength

~7.4 MPa (~1073 psi)

(ASTM D638)

Pull-Off Strength

> 2.5 MPa (> 363 psi) (substrate failure)

(ASTM D7234)

Coefficient of Friction

~0.41 Wet

(ANSI A137.1 / ANSI A326.3)

~0.96 Dry(DCOF - BOT 3000e)

Service Temperature

Minimum 0 °C (32 °F)  Maximum 50 °C (122 °F)

Temperature Resistance

Flammability:

~35 mm (~1.37 in)

(ASTM D635)

Thermal Compatibility

Passes

(ASTM C884)

Water Absorption

~0.3 %

(ASTM C413)

Chemical Resistance

Consult Sika Canada

Application

Application Information

Mixing Ratio

A:B = 2:1 by volume

Product Temperature

Condition product at temperatures between 18 °C to 30 °C (65 °F to 86 °F) before using.

Ambient Air Temperature

Minimum 10 °C (50 °F). Maximum 30 °C (85 °F).
Mixing and application attempted at material, ambient and/or substrate temperature conditions less than 18 °C (65 °F) will result in a decrease in product workability and slower cure rates.

Relative Air Humidity

Maximum 85 % (during application and curing).

Dew Point

Substrate must be at least 3 ˚C (5 ˚F) above the Dew Point to reduce the risk of condensation, which may lead to adhesion failure or “blushing” on the floor finish.

Substrate Moisture Content

Moisture content of concrete substrate must be ≤ 4 % by mass (pbw – part by weight) as measured with a Tramex®CME / CMExpert type concrete moisture meter.

Pot Life

250 g (8.8 oz)

10 °C (50 °F)

20 °C (68 °F)

30 °C (86 °F)

Open time in pot

~60 minutes

~40 minutes

~15 minutes

Open time on substrate

~80 minutes

~50 minutes

~35 minutes

Curing Time

10 °C (50 °F)

20 °C (68 °F)

30 °C (86 °F)

Foot traffic

~2 days

~1 day

~18 hours

Light traffic

~4 days

~2 days

~2 days

Waiting Time / Overcoating

10 °C (50 °F)

20 °C (68 °F)

30 °C (86 °F)

Minimum

~30 hours

~8 hours

~6 hours

Maximum~72 hours~48 hours~24 hours

Applied Product Ready for Use

10 °C (50 °F)

20 °C (68 °F)

30 °C (86 °F)

Full Cure /

Chemical Exposure

~10 days

~7 days

~5 days
Consumption

Consumption

Prime coat

Sikafloor®-261CA (regular)
5 m2/L (200 ft2/US gal.) (8 mil w.f.t.)

Thixo Lite wear coat

Sikafloor®-261 CA Thixo Lite (special component B)
4.4 m2/L to 6.6 m2/L (178 ft2/ US gal. to 267 ft2/ US gal.) (6 to 9 mil w.f.t.)

Actual coverage rates and material consumption will depend upon porosity and profile of substrates. Allowance must be also made for variation in film thickness or number of coats required to achieve opacity with light (i.e. white) or bright colours (i.e. reds and yellows) on dark substrates. Test sections are recommended to establish correct coverage.
Application steps

MIXING

Mixing Ratio (A:B) = 2:1 by voilume

Do not hand mix Sikafloor® materials. Mechanically mix only.  

Pre-mix each component separately. Empty component B in the correct mix ratio to component A. Mix the combined components for at least three (3) minutes, using a low-speed drill (300 - 450 rpm) to minimize entrapping air.

Use an Exomixer® type mixing paddle (recommended model) suited to the volume of the mixing container.

During the mixing operation, scrape down the sides and bottom of the container with a flat or straight edge trowel at least once to ensure complete mixing. When completely mixed, Sikafloor®-261 CA Thixo Lite prime coat (regular) and thixo lite wear coat (special component B) should be uniform in colour and consistency.

Mix only that quantity which can be used within its pot life.  

APPLICATION

Prime Coat: Apply standard viscosity Sikafloor®-261 CA as a primer onto the substrate using a brush, roller or squeegee, at a uniform coverage without puddling.

Thixo Lite Wear Coat: Once prime coat is tack-free, apply the thixo lite wear coat using a squeegee or roller and backroll to achieve even coverage. Finish with a high quality, lint-free, short nap roller (6 mm) to achieve the desired surface texture. The texture peak through height will vary depending on the mil thickness and type of roller used.

CLEAN UP

Clean all tools and equipment with Sika® Epoxy Cleaner. Once hardened, product can only be removed mechanically.